CHEMICAL
COMPOSITION ( IN PERCENTAGE ) |
Grade |
C (Max) |
Mn (Max) |
P (Max) S (Max) |
Si (Max) |
Cr Ni |
Mo |
Nitrogen (Max) |
Cu/ Others |
301 |
0.15 |
2.00 |
0.045
0.030 |
1.00 |
16.00
- 18.00 6.00 - 8.00 |
- |
0.10 |
- |
304 |
0.08 |
2.00 |
0.045 0.030 |
0.75 |
18.00 - 20.00 8.00- 10.50 |
- |
0.10 |
- |
304L |
0.030 |
2.00 |
0.045
0.030 |
0.75 |
18.00
- 20.00 8.00- 12.00 |
- |
0.10 |
- |
310S |
0.08 |
2.00 |
0.045 0.030 |
1.50 |
24.00- 26.00 19.00 - 22.00 |
- |
- |
- |
316 |
0.08 |
2.00 |
0.045
0.030 |
0.75 |
16.00
- 18.00 10.00 - 14.00 |
2.00 -
3.00 |
0.10 |
- |
316L |
0.030 |
2.00 |
0.045 0.030 |
0.75 |
16.00 - 18.00 10.00 - 14.00 |
2.00 - 3.00 |
0.10 |
- |
317 |
0.08 |
2.00 |
0.045
0.030 |
0.75 |
18.00
- 20.00 11.00 - 14.00 |
3.00 -
4.00 |
0.10 |
- |
317L |
0.030 |
2.00 |
0.045 0.030 |
0.75 |
18.00 - 20.00 11.00 - 15.00 |
3.00 - 4.00 |
0.10 |
- |
321 |
0.08 |
2.00 |
0.045
0.030 |
0.75 |
17.00
- 19.00 9.00 - 12.00 |
- |
0.10 |
Ti5 (
C + N ) Min or 0.70 max |
347H |
0.08 |
2.00 |
0.045 0.030 |
0.75 |
17.00 - 19.00 9.00 - 13.00 |
- |
- |
Cb= 10x ( C Min ) or 1.00 Max |
409 |
0.08 |
1.00 |
0.040
0.010 |
1.00 |
10.50
- 11.75 0.50 |
- |
- |
Ti=
6x (C+ N ) Min or 0.70 Max |
409M |
0.03 |
0.81.2 |
0.030 0.030 |
0.40.75 |
11.00- 12.00 1.5 max. |
- |
- |
Ti= 6x (C) Min or 0.70 Max |
410S |
0.08 |
1.00 |
0.040
0.030 |
1.00 |
11.50- 13.50 0.60 |
- |
- |
- |
410 |
0.15 |
1.00 |
0.040 0.030 |
1.00 |
11.50- 13.50 0.75 |
- |
- |
- |
420 |
0.35 |
0.50 |
0.035
0.015 |
0.50 |
12.00
- 13.00 0.20.3 |
- |
- |
- |
430 |
0.12 |
1.00 |
0.040 0.030 |
1.00 |
16.00 - 18.00 0.75 |
- |
- |
- |
JSL
AUS |
0.08 |
7.08.0 |
0.070
0.030 |
0.75 |
15.50
- 16.50 4.25 - 4.75 |
- |
- |
0.9 -
1.10 |
JS- 203 |
0.08 |
9.2510.25 |
0.070 0.030 |
0.75 |
14.25 - 15.25 2.25 - 2.75 |
- |
- |
1.60- 2.0 |
301M |
0.10 |
4.55.5 |
0.060
0.030 |
0.75 |
14.50
- 15.50 6.0 - 7.0 |
- |
- |
1.70-
1.90 |